Philips SPC900NC fix
Would not have passed final testing , like that, at production. Probably
close but seaparate solder joints that would have passed final tests, that
over time bridged with tin-whiskers.
Any idea of date of production ?
Not sure - is there a way to tell?
, if later than 2006 then much more likely
tin-whisker growing conditions. Although aerospace is a derogated
industry,
outside of Wee/RoHS and can use proper solder, astronomical telescopes
would not be covered by that derogation.
|